Chalybum liberum secans vel immaculatum machinatio chalybis est genus offensionis chalybis, in quo sulphur, plumbum, calcium, selenium, tellurium, aliaque elementa libera incisa adduntur ad facultatem sectionis emendandam. Haec elementum liberum secans componit ascias praeligato et reducit ad resistentiam ferro immaculati secans, ita reducens asperitatem et instrumentum vitae servitii melioris usque ad celeritates incisas et profunditatem maiorem incisionis. Chalybes gratis incisis immaculatus late in partibus machinae adhibitis quae corrosionem resistentiae requirunt et incisionem liberam.
Communis usus sine ferro incisis incorrupta maxime includit Austenite SUS303 ; 430F, Martensite 410F2, 416, SUS 420F2. Sulphur contentum plus quam 0.3% additis SUS303 et 430 machinabilitatem emendare est, sed nimis altum sulphur resistentiae corrosionis reducet et aliae notae, ita unumquodque liberum elementum sectionis familiae secundum optimam compositionem adici debet. Summam quantitatem liberae elementorum sectionis augere debemus ac deminutionem notarum ad minimum gradum finire. S et Pb, Se et Te in Ferrite et Martensite vulgatis addunt.
Austenitic Aliquam Steel Gradibus
UNS | C | Si | Mn | P | S | Cr | Ni | Mo | Se | Cu | Al |
S20300
XIII-1 |
≤0.08 | ≤1.00 | 5.00-
6.50 |
≤0.04 | 0.18
0.35 |
16.00
18.00 |
5.00
6.50 |
/ | / | 1.75
2.25 |
/ |
S30300
303 |
≤0.15 | ≤1.00 | ≤2.00 | ≤0.20 | ≥0.15 | 17.00
19.00 |
8.00
10.00 |
/ | / | / | / |
S30310
XIII-5 |
≤0.15 | ≤1.00 | 2.5-
4.5 |
≤0.20 | ≥0.25 | 17.00
19.00 |
7.00
10.00 |
/ | / | / | / |
S30323
303se |
≤0.15 | ≤1.00 | ≤2.00 | ≤0.20 | ≤0.06 | 17.00
19.00 |
8.00
10.00 |
/ | ≥0.15 | / | / |
S30345
XIII-2 |
≤0.15 | ≤1.00 | ≤2.00 | ≤0.05 | 0.11
0.16 |
17.00
19.00 |
8.00
10.00 |
0.40
0.60 |
/ | / | 0.60
1.00 |
martensitic Aliquam Steel Gradibus
UNS | C | Si | Mn | P | S | Cr | Ni | Se | Cu |
S41600
416 |
≤0.15 | ≤1.00 | ≤1.25 | ≤0.06 | ≥0.15 | 12.00
14.00 |
/ | / | / |
S41610
XIII-6 |
≤0.15 | ≤1.00 | 1.50
2.50 |
≤0.06 | ≥0.15 | 12.00
14.00 |
/ | / | / |
S41623
416se |
≤0.15 | ≤1.00 | ≤1.25 | ≤0.06 | ≤0.06 | 12.00
14.00 |
/ | ≥0.15 | / |
S42020
420F |
0.30
0.40 |
≤1.00 | ≤1.25 | ≤0.06 | ≥0.15 | 12.00
14.00 |
(≤0.5) | / | (≤0.6) |
S44020
440F |
0.95
1.20 |
≤1.00 | ≤1.25 | ≤0.06 | ≥0.15 | 16.00
18.00 |
(≤0.5) | / | (≤0.6) |
Feritic Aliquam Steel Gradibus
UNS | C | Si | Mn | P | S | Cr | Ni | Mo | Se | Ti | N |
S18200
XIII-34 |
≤0.08 | ≤1.00 | ≤2.50 | ≤0.04 | ≥0.15 | 17.50
19.50 |
/ | 1.50
2.50 |
/ | / | / |
S18235 | ≤0.025 | ≤1.00 | ≤0.50 | ≤0.03 | 0.15
0.35 |
17.50
18.50 |
≤1.00 | 2.00
2.50 |
/ | 0.30
1.00 |
≤0.025注 |
S41603 | ≤0.08 | ≤1.00 | ≤1.25 | ≤0.06 | ≥0.15 | 12.00
14.00 |
/ | / | / | / | / |
S43020
430F |
≤0.12 | ≤1.00 | ≤1.25 | ≤0.06 | ≥0.15 | 16.00
18.00 |
/ | / | / | / | / |
S43023
430FSe |
≤0.12 | ≤1.00 | ≤1.25 | ≤0.06 | ≤0.06 | 16.00
18.00 |
/ | / | ≥0.15 | / |
(Nota:C+N≤0.035)